Places of Usage
• It is used in multi-storey and underground car parks, storage areas, maintenance hangars, such as places exposed to moderate to heavy mechanical effects; where resistance to chemicals is required such as chemical production facilities, laboratories; in places where aesthetics, easy maintenance and cleaning are important such as shopping malls, exhibition areas, fairgrounds and in places not exposed to sunlight. Used indoors, on horizontal surfaces.
Features/ Advantages
• It can mix filler in 1 :1 rate depending on the desired application thickness.
• Thanks to its low viscosity, the comb marks that are formed during the application disappear quickly and a smooth appearance is obtained.
• High mechanical resistance.
■ High chemical resistance.
• It is liquid impermeable.
• It is aesthetic thanks to its wide color choice and bright finish.
• Long life and easy to clean.
• Solvent-free, eco friendly.
Application Directions
a) Surface Preparation:
The surface must be dry, clean, free of strong skate; oil, dirt or adhesion preventive materials must be removed from the surface; materials such as mortar, cement residues should be scraped. Before applying the primer on the surface, an open porous structure should be formed on the cement top layer by using surface abrasive equipment (Shotblast, Rototiger etc). Dusting should be cleaned with industrial vacuum cleaner. The abraded concrete surface should have a minimum compressive strength of 25 N/mm' and a tensile strength of 1 .5 N/mm'. Ensure that surface moisture, relative humidity and dew point requirements are met before application. Otherwise, the desired performance criteria cannot be reached from the product as a result of carbonation reaction on the surface. Moisture content of the surface should be maximum 4%. Relative humidity should be maximum 80%.
b) Product Preparation:
21 kg is packaged in appropriate quantities. Each component is first mixed in itself. Component B (Hardener) is added to component A (Epoxy resin). It is mixed with a drill with 300 - 400 rpm mixer tip for 3-4 minutes until a homogenous consistency is obtained. The entire mixture is then taken to a clean container and mixed again. If part of the product is to be used, these mixing ratios should be considered. The dew point should be above+ 3 ° C
before and afterthe application in order to prevent the formation of condensation. New concrete structures should be allowed to dry for a minimum of 28 days. Repair of surface defects with a depth of more than 1 cm should be done with Neroflex Epoxy Repair Mortar or Neroflex Grout Mortar 6-8 hours in advance. After surface cleaning, it should be primed with Neroflex Primer in single or double layers depending on the condition of the surface in order to increase the adhesion strength and balance the surface absorbency. Depending on the porosity and structure of the surface, the surface can be leveled with the addition of a filler. Depending on the porosity and structure of the surface, the surface can be leveled with the addition of filler. On surfaces that are moist up to 10%, it should be applied with Neroflex Primer, otherwise the application should not be done. At least 20 minutes after the primer application, sand blasting is performed with appropriate filler until the product reaches saturation, the adhesion strength of the floor covering to be applied after itself must be increased, please refer to consumption table for recommended fill amount. In order to apply N8007 Epoxy Self application, the sanding primer must have gained the hardness. Please refer to the technical data sheet of the primer used, as the opening time may vary with temperature. After primer sandblasting, non-adherent fillings should be removed by sweeping or industrial brom.                c)Application Method:
N8007 Epoksi Self prepared mixture should be poured onto the surface and spread with the help of a notched trowel. The spiked roller should be passed over perpendicular to each other and the remaining air bubbles should be removed and the coating thickness should be balanced. In order to obtain a non-slip, blunted surface, the first sandblasting after 15 to 20 minutes following the above application, and after a maximum of 30 minutes after spreading with quartz filler, a non-slip, blunted surface should be obtained. Please refer to Consumption table for the recommended fill amount.
Issues to be Considered
■ Avoid application at temperatures below +10°C and above+ 30"C.
• Can be applied outdoors, but no color stability.
• When mixing 8007 Epoksi Self, a suitable drill must be used. Never mix with hand or trowel.
• Do not add water, solvent, etc. to the mixture externally. Do not dilute with thinner, etc.
• Materials should be brought to the application area at least 24 hours before the application to comply with the environmental conditions.
• The working and curing times of epoxy resin based products depend on the ambient and floor temperature. Consumption amount increases as viscosity increases at low temperatures. The chemical reaction slows down, thus the pot life and working time prolongs. At high temperatures, the opposite is the case.
• If heating is required in the application area, only electrical, warm air blower systems should be used not to affect the appearance of the surface.
• Avoid application in areas that are frozen, at risk of freezing within 24 hours or exposed to direct sun and wind.
• Do not step on at least 24 hours after application. Avoid water contact and condensation for 48 hours, otherwise carbonation occurs. In this case, the surfaces are cleaned with sandpaper and a thin coat is applied again.
Cleaning of Tools:
Tools and equipment used should be cleaned with water after the application. 8007 Epoksi Self can only be removed mechanically from the surface after hardening.
Storage
Maximum 3 palettes should be placed on top of each other and should be stored in a dry environment.
Consumption    See the consumption table.
Package   In 21 kg (A+B) set plastic buckets.
N8007 Epoxy Self
Quality Certificates: Manufactured according to TS EN 13813   TS EN 1504-2